our company offer a complete "white metal bearings" and machining service for connecting rods, main bearings, and thrust bearings.Both direct cast and shell big end bearings, direct cast and shell main bearings, thrust bearings, split or one part bearings can be dealt with.Solid white metal bearings can also be manufactured. If necessary new backing shells can be manufactured.

Bearing refurbishment can offer significant savings and time compared to an abrupt order of new bearings. But there are many factors involved to ensure a completely successful repair of a white metal bearings, such as an extensive knowledge of oil film lubrication. It took our specialised bearing partner only 6 days to repair the three white metal bearings!

Here we see an example of rough cast white metal main bearings, ready to be fitted into a crank case where they be line bored perfectly in line to exact sizes as determined by the newly ground crank shaft to be fitted in this engine.

When you have reached the proper temperature for your Babbitt, you should skim the dross from the heating container. In most cases this nsk bearings can be done easily. Failure to remove the dross will result in a weakened Babbitt bearing and can cause poor formation and premature failure.

Once all dross is removed, you can begin the pouring process. Using a ladle is an ideal way to pour Babbitt. Pouring should be done quickly and in one motion if at all possible. Pouring too slowly can result in a poor bond and sub-par performance in the final piece.

It's not going to as quickly grab the edge of the yo-yo. It's going to be centered there. It allows you to do tricks at much longer time, allows everything to keep smooth and what not. So those are your basic types of nachi bearings. You can also get different ABEC ratings, there's ABEC five and seven just kinda like skateboards. There's even ceramic bearings. Ceramic bearings spin for an incredibly long time, it's not incredibly needed though. 